RESUMO
Aim: The roughness and micromorphology of various surface treatments in aged metal-free crowns and the bond strength of these crowns repaired with composite resin (CR) was evaluated in vitro. Methods: A CR core build-up was confectioned in 60 premolars and prepared for metal-free crowns. Prepared teeth were molded with the addition of silicone, and the laboratory ceromer/fiber-reinforced crowns (SR Adoro/Fibrex Lab) were fabricated. Subsequently, the crowns were cemented and artificially aged in a mechanical fatigue device (1.2 X 106 cycles), then divided into 4 groups (n = 15) according to the surface treatment: 1) phosphoric acid etching (PA); 2) PA + silane application; 3) roughening with a diamond bur + PA; and 4) sandblasting with Al2O3 + PA. After the treatments, the crowns (n = 2) were qualitatively analyzed by scanning electron microscope (SEM) and surface roughness (n = 5) was analyzed before and after the surface treatment (Ra parameter). The remaining crowns (n = 8) received standard repair with an adhesive system (Tetric N-Bond) and a nanohybrid CR (Tetric N-Ceram), and the microshear bond strength (SBS) test was performed (0.5 mm/min). Roughness and SBS data were analyzed by one- and two-way ANOVA, respectively, as well as Tukey's post-test (α = 0.05). Results: Sandblasting with Al2O3 + PA resulted in the highest final roughness and SBS values. The lowest results were observed in the PA group, whereas the silane and diamond bur groups showed intermediate values. Conclusion: It may be concluded that indirect ceromer crowns sandblasted with aluminum oxide prior to PA etching promote increased roughness surface and bond strength values